Film Type
Biaxially Oriented Polypropylene
Film Thickness
1.8mils (nominal)
Adhesive
Emulsion Acrylic
Tensil
22 lbs/in
Elongation
140 (% at break)
Application Temperature
32° to 140° F
Operating Temperature
-10° to 200° F – normal range
Polypropylene tape water based acrylic adhesive
Use for bundling and sealing light to medium weight cartons in a wide range of temperatures where STA’s uniquely formulated age-resistant/non-yelling, fiber pulling acrylic adhesive is required.
Other Standards and Specifications
Conforms to FDA SPECS: 21 CFR 175.105 and CFR177.1520 for indirect food contact, (Clear tape only). Complies with environmental considerations of ASTM D 1974-14.
The conditions at which the tape is unwound and applied to the substrate. Under normal conditions the tape should unwind and adhere to the substrate properly, and perform as normally expected. The tape should be used within 1 year of the date of shipment.Application & Operating Conditions
Notes: *Shear is the tape’s ability to resist the sliding of two substrates relative to each other’s planes of contact. (to hold flaps down). The information listed above has been obtained from controlled laboratory tests and is reliable, but should not be used for the purpose of writing specifications. It is offered in good faith, but without guarantee, as conditions and methods of use of STA products are beyond STA’s control. It is recommended that the prospective user determine their suitability before adapting them on a commercial scale.
*Pressure Tape Council
***ASTM Standard D3330, “Standard Test Method for Peel Adhesion of Pressure Sensitive Tapes”
**ASTM Standard D3759, “Standard Test Method for Tensile Strength and Elongation of Pressure Sensitive Tapes”
ASTM International, West Conshohocken, PA. www.astm.org